Skip to main content

NOTICE: Due to a lapse in annual appropriations, most of this website is not being updated. Learn more.

Form submissions will still be accepted but will not receive responses at this time. Sections of this site for programs using non-appropriated funds (such as NVLAP) or those that are excepted from the shutdown (such as CHIPS and NVD) will continue to be updated.

U.S. flag

An official website of the United States government

Official websites use .gov
A .gov website belongs to an official government organization in the United States.

Secure .gov websites use HTTPS
A lock ( ) or https:// means you’ve safely connected to the .gov website. Share sensitive information only on official, secure websites.

Porosity, Powder X-Ray Diffraction Patterns, Skeletal Density, and Thermal Stability of NIST Zeolitic Reference Materials RM 8850, RM 8851, and RM 8852

Published

Author(s)

Huong Giang Nguyen, Ran Tao, Roger D. van Zee

Abstract

This paper reports the powder X-ray diffraction patterns, argon isotherms at 87 K, Brunauer–Emmett–Teller surface areas, pore size distributions, pore volumes, skeletal densities, and thermal gravimetric analyses for three National Institute of Standards and Technology zeolitic reference materials, RM 8850 (zeolite Y), RM 8851 (zeolite A), and RM 8852 (ZSM-5).
Citation
Journal of Research (NIST JRES) -
Volume
126

Keywords

characterization, RM 8850, RM 8851, RM 8852, zeolite A, zeolite Y, ZSM-5

Citation

Nguyen, H. , Tao, R. and van Zee, R. (2022), Porosity, Powder X-Ray Diffraction Patterns, Skeletal Density, and Thermal Stability of NIST Zeolitic Reference Materials RM 8850, RM 8851, and RM 8852, Journal of Research (NIST JRES), National Institute of Standards and Technology, Gaithersburg, MD, [online], https://doi.org/10.6028/jres.126.047, https://tsapps.nist.gov/publication/get_pdf.cfm?pub_id=933466 (Accessed October 2, 2025)

Issues

If you have any questions about this publication or are having problems accessing it, please contact [email protected].