Influence of Elastic-Electron Scattering on Measurements of Sillicon Dioxide Film Thicknesses by X-Ray Photoelectron Spectroscopy

Published

Author(s)

Cedric J. Powell, Aleksander Jablonski

Abstract

We investigate the systematic error due to neglet of elastic scattering of photoelectrons in measurements of the thicknesses of thin films of SiO2 on Si by x-ray photoelectron spectroscopy (XPS). Calulations were made of substrate Si 2p photoelectron currents excited by characteristic Mg and Al Kα x rays for different SiO2 thicknesses, different angles of photoelectron emission, and three representative XPS configurations using an algorithm based on the transport approximation. We calculated practical effective attenuation lengths (EALs) from changes of the computed Si 2p photoelectron currents. These EALs were less than the corresponding inelastic mean free paths by between 6.5% and 9.4%, with the difference depending on the x-ray source, the specific range of SiO2 film thicknesses under consideration, the XPS configuration, and the range of photoelectron emission angles. Useful average values of the EAL were found for emission angles between 0 and about 60 (with respect to the surface normal) and for silicon dioxide thicknesses such that the substrate signal was not attenuated to not more than 1% and 10% of its original value. Our calculated EALs are in satisfactory agreement with measured EALs. For larger emission angles, the calculated EALs change rapidly with SiO2 thickness and specific values should be found for the conditions of interest.
Citation
Journal of Vacuum Science and Technology A
Volume
19
Issue
No. 5

Keywords

effective attenuation length, elastic-electron scattering, film thickness, silicon, silicon dioxide, x-ray photoelectron spectroscopy

Citation

Powell, C. and Jablonski, A. (2001), Influence of Elastic-Electron Scattering on Measurements of Sillicon Dioxide Film Thicknesses by X-Ray Photoelectron Spectroscopy, Journal of Vacuum Science and Technology A (Accessed May 24, 2024)