The Effect of Stress Induced Anisotropy in Patterned FeCo Thin Film Structures

Published

Author(s)

W Yu, J A. Bain, Willard C. Uhlig, John Unguris

Abstract

In this work, 1 υm thick FeCeo films with -320 MPa compressive stress and FeCo/NiFe films with 600 MPa tensile stress were patterened into 5υm x 20 υm elements. The stress anisotropy resulting from patterning was measured using x-ray diffraction to be 220 MPa for the tensile films and -170 MPa for the compressive films and are in afreement with the finite element modelling. SEMPA imaging shows that the domain structure of the elements was influenced by the stress induced anisotropy. Calculattions of the effect of stress anisotropy were performed on domain congurations for the patterened structures. Results indicate that tensile stresses should reinforce closure domains, while compressive stresses of magnitude greater than 50 MPa should result in easy axis rotation, and is in agreement with the experimental results.
Citation
Journal of Applied Physics
Volume
99
Issue
8

Keywords

FeCo, magnetic domains, NiFe, patterned films, stress

Citation

Yu, W. , Bain, J. , Uhlig, W. and Unguris, J. (2006), The Effect of Stress Induced Anisotropy in Patterned FeCo Thin Film Structures, Journal of Applied Physics (Accessed March 28, 2024)
Created April 23, 2006, Updated October 12, 2021