Unraveling the Stable Cathode Electrolyte Interface in all Solid-State Thin-Film Battery Operating at 5 V

Published

Author(s)

Ryosuke Shimizu, Diyi Cheng, Jamie Weaver, Minghao Zhang, Bingyu Lu, Thomas Wynn, Randall Burger, Min-cheol Kim, Guomin Zhu, Ying Shirley Meng

Abstract

Spinel-type LiNi0.5Mn1.5O4 (LNMO) is one of the most promising 5 V-class cathode materials for Li-ion batteries that can achieve high energy density and low production costs. However, in liquid electrolyte cells, the high voltage causes continuous cell degradation through the oxidative decomposition of carbonate-based liquid electrolytes. In contrast, some solid-state electrolytes have a wide electrochemical stability range and can withstand the required oxidative potential. In this work, a thin-film battery consisting of an LNMO cathode with a solid lithium phosphorus oxynitride (LiPON) electrolyte is tested and their interface before and after cycling is characterized. With Li metal as the anode, this system can deliver stable performance for 600 cycles with an average Coulombic efficiency >99%. Neutron depth profiling indi-cates a slight overlithiated layer at the interface prior to cycling, a result that is consistent with the excess charge capacity measured during the first cycle. Cryogenic electron microscopy further reveals intimate contact between LNMO and LiPON without noticeable structure and chemical composition evolution after extended cycling, demonstrating the superior stability of LiPON against a high voltage cathode. Consequently, design guidelines are proposed for interface engineering that can accelerate the commercialization of a high voltage cell with solid or liquid electrolytes.
Citation
Advanced Energy Materials

Keywords

Li-ion, NDP, interface, soild-state, battery

Citation

Shimizu, R. , Cheng, D. , Weaver, J. , Zhang, M. , Lu, B. , Wynn, T. , Burger, R. , Kim, M. , Zhu, G. and Meng, Y. (2022), Unraveling the Stable Cathode Electrolyte Interface in all Solid-State Thin-Film Battery Operating at 5 V, Advanced Energy Materials, [online], https://doi.org/10.1002/aenm.202201119, https://tsapps.nist.gov/publication/get_pdf.cfm?pub_id=934384 (Accessed December 9, 2022)