Crystallization of Polyethylene Oxide Patterend by Nanoimprint Lithography



Brian C. Okerberg, Christopher L. Soles, Jack F. Douglas, Hyun Wook Ro, Alamgir Karim


The crystallization behavior of poly(ethylene oxide) (PEO) films patterned by nanoimprint lithography is studied. The imprinted PEO film consists of parallel lines, approximately 240 nm wide and 320 nm tall, on a 400 nm pitch with a residual layer of approximately 10 nm. A spherulitic superstructure, typically observed for bulk PEO samples, is observed by optical microscopy. This result indicates that the crystal lamellae communicate through the continuous thin residual layer into discrete patterned regions that span hundreds of micrometers. In the discrete imprinted lines, the lamellae generally have a flat-on orientation with respect to the substrate. When the radial growth direction of the spherulite is parallel to the lines, a terraced morphology develops where the lamellae grow largely unperturbed along the imprinted line direction. When the radial growth direction is orthogonal to the lines, the lamellae are also elongated along the imprint line direction, suggesting that the crystal growth direction within the lines is orthogonal to the spherulite growth direction. The mold walls do not significantly influence the orientation of the lamellae suggesting that the orientation of the lamellae is determined in the early stages of crystallization.


confinement, crystallization, lithography, morphology, nanoimprint, PEO, spherulite


Okerberg, B. , Soles, C. , Douglas, J. , , H. and Karim, A. (2007), Crystallization of Polyethylene Oxide Patterend by Nanoimprint Lithography, Macromolecules, [online], (Accessed April 19, 2024)