NOTICE: Due to a lapse in annual appropriations, most of this website is not being updated. Learn more.

Form submissions will still be accepted but will not receive responses at this time. Sections of this site for programs using non-appropriated funds (such as NVLAP) or those that are excepted from the shutdown (such as CHIPS and NVD) will continue to be updated.

U.S. flag

An official website of the United States government

Official websites use .gov
A .gov website belongs to an official government organization in the United States.

Secure .gov websites use HTTPS
A lock ( ) or https:// means you’ve safely connected to the .gov website. Share sensitive information only on official, secure websites.

PUBLICATIONS

Environmentally Enhanced Crack Growth in AlN

Published

Author(s)

Roy W. Rice, C C. Wu, K R. McKinney, Stephen W. Freiman, L E. Dolhert, J H. Enloe

Abstract

Three tests: (1) dynamic fatigue; (2) flexure strength, and (3) direct, double-cantilever beam stress intensity-crack velocity measurements carried out in air (22 C) and liquid nitrogen (-196 C) all showed that dense sintered AlN undergoes slow crack growth (SCG) in air at room temperature. These and other results from the literature indicate that SCG in AlN occurs intergranularly due to moisture. The severity of the SCG varies from that of Al2O3 (e.g. n values of 20-60) to N values of several hundred or more. A comparison with data on SiC and Si3N4 indicate that SCG in AlN occurs due to residual oxide additives in grain boundary, but no clear distinction was observed between AlN densified with CaO or Y2O3 additions. Testing of AlN samples which had undergone surface (post fired) or cofired (e.g. via) metallization showed significant strength reductions rather than increases in testing at - 196 C, but metallized samples immersed in liquid nitrogen without testing, removed, and then tested in air at 22 C showed no strength decrease, indicating that the lower strengths in liquid nitrogen were due to added thermal expansion mismatch stresses between the metallization and AlN, not the formation of cracks due to the stresses.
Citation
International Journal of Applied Ceramic Technology
Pub Type
Journals

Keywords

aluminum nitride, fracture mode, grain boundary phases, slow crack growth
Ceramics and Biomaterials

Citation

Rice, R. , Wu, C. , McKinney, K. , Freiman, S. , Dolhert, L. and Enloe, J. (2021), Environmentally Enhanced Crack Growth in AlN, International Journal of Applied Ceramic Technology (Accessed October 10, 2025)