Elastic Modulus Characterization of Nanocomposite Latex Coatings
Published
Author(s)
Aaron M. Forster, Stephanie S. Watson, Jonathan White
Abstract
The elastic modulus of a polystyrene-butyl acrylate latex coating was measured using three different techniques: instrumented indentation, dynamic mechanical analysis, and tensile testing. The coating was formulated with 25 nm and 250 nm diameter TiO2 particles at three different pigment volume concentrations (PVC). Additional coatings were formulated with sol-gel created TiO2 and ZnO particles at 2.5 % PVC. Indentation consistently measured a higher modulus than DMA or tensile testing. All three metrologies agreed after the elastic modulus was normalized by the unfilled coating modulus. Nanoparticles produced less of an improvement in the elastic modulus than 250 nm particles. Existing theoretical models for normalized modulus were used to infer the particle dispersion in the coating.
Forster, A.
, Watson, S.
and White, J.
(2008),
Elastic Modulus Characterization of Nanocomposite Latex Coatings, Nanotechnology Applications in Coatings, Oxford University Press, New York, NY