NOTICE: Due to a lapse in annual appropriations, most of this website is not being updated. Learn more.

Form submissions will still be accepted but will not receive responses at this time. Sections of this site for programs using non-appropriated funds (such as NVLAP) or those that are excepted from the shutdown (such as CHIPS and NVD) will continue to be updated.

U.S. flag

An official website of the United States government

Official websites use .gov
A .gov website belongs to an official government organization in the United States.

Secure .gov websites use HTTPS
A lock ( ) or https:// means you’ve safely connected to the .gov website. Share sensitive information only on official, secure websites.

PUBLICATIONS

Unraveling the Complex Hydration Behavior of Ionomers Under Thin Film Confinement

Published

Author(s)

Shudipto K. Dishari, Christopher A. Rumble, Mark Maroncelli, Joseph Dura, Michael A. Hickner

Abstract

Ionomers in thin films behave differently from bulk membranes and their behavior is not well understood. Here, thin films (25-250 nm) of sulfonated Radel (S-Radel) were investigated to understand thickness and hydration effects on the density and mechanical properties of these sulfonated thin polymer films. The density values obtained from quartz crystal microbalance and spectroscopic ellipsometry showed a thickness trend similar to density values obtained from neutron reflectometry with thin films of 25 nm thickness having lower densities than thicker, 250 nm films. Thicker films were always more dense and less water-rich at the interface compared to thinner samples. A fluorescent rotor probe was incorporated into the polymer samples to infer material stiffness from fluorescence lifetime measurements. The lower density from ellipsometry and neutron reflectometry rationalized greater mobility from fluorescence measurements in the thinner films when dry. When the thin sample was hydrated, the film density and interfacial water volume fraction significantly increased. Also the samples with lower thickness antiplasticized indicating poor water-polymer mobility inside the film. The plasticization properties appeared to be controlled by both film density and water-polymer mobility. The complex hydration behavior of thin ionomer films in the confined state is described in this work.
Citation
Journal of Physical Chemistry C
Volume
122
Pub Type
Journals

Download Paper

Local Download

Keywords

polymer electrolyte, neutron reflectometry, mobility, interface, anitplasticization
Materials

Citation

Dishari, S. , Rumble, C. , Maroncelli, M. , Dura, J. and Hickner, M. (2018), Unraveling the Complex Hydration Behavior of Ionomers Under Thin Film Confinement, Journal of Physical Chemistry C, [online], https://tsapps.nist.gov/publication/get_pdf.cfm?pub_id=922152 (Accessed October 17, 2025)