Deep-Penetrating Conical Cracks in Brittle Layers from Hydraulic Cyclic Contact

Published

Author(s)

Yu Zhang, Jun-Feng Song, Brian R. Lawn

Abstract

A study is made of fracture from cyclic loading of WC spheres on the top surfaces of thick (1 mm) brittle layers on polymeric substrates, as representative of repetitive occlusal contact on dental crown structures. The advantage of glass layers is that internal cracks can be followed in situ during the entire cyclic loading process. The glass surfaces are first given a surface abrasion treatment to control the flaw state, such that the strengths match those of dental porcelains. Cyclic contact tests are carried out at prescribed maximum loads and frequencies, in water. In addition to conventional cone cracks that form outside the contact circle, additional, inner cone cracks form within the contact. These inner cones are observed only in cyclic loading, and are accelerated at higher frequencies, indicating a strong mechanical driving force. They tend to initiate after the outer cones, but subsequently catch up and penetrate much more rapidly and deeply, ultimately intersecting the underlying coating/substrate interface. Comparative tests on glass/polymer bilayers versus monolithic glass, in cyclic versus static loading, in water versus air environment, on abraded versus etched surfaces, and with glass instead of WC indenters, confirm the existence of a dominant mechanical element in the inner cone crack evolution. It is argued that this new type of cone cracking can limit dental crown veneer lifetimes under occlusal fatigue conditions, especially in thicker layers where competing modes such as undersurface radial cracks are suppressed.
Citation
Journal of Biomedical Materials Research
Volume
73B
Issue
No. 1

Keywords

biomechanical ceramics, cone cracks, contact damage, cyclic fatigue, fracture modes, glass

Citation

Zhang, Y. , Song, J. and Lawn, B. (2005), Deep-Penetrating Conical Cracks in Brittle Layers from Hydraulic Cyclic Contact, Journal of Biomedical Materials Research (Accessed April 15, 2024)
Created January 1, 2005, Updated February 17, 2017