Publication Citation: Phase Equilibria and Dielectric Behavior in the CaO:Al2O3:Nb2O5 System

NIST Authors in Bold

Author(s): Terrell A. Vanderah; W Febo; Julia Y. Chan; Robert S. Roth; J. M. Loezos; L D. Rotter; Richard G. Geyer; B A. Reisner; Dennis B. Minor;
Title: Phase Equilibria and Dielectric Behavior in the CaO:Al2O3:Nb2O5 System
Published: November 01, 2000
Abstract: Subsolidus phase equilibria in the CaO:Al2O3:Nb2O5 system at 1325 C in air have been determined. One ternary phase forms, Ca2AlNbO6, which exhibits a perovskite-related structure with 1:1 or NaCl-type ordering of Al3+ and Nb5+ on the B-sites. Indexed X-ray powder diffraction data for this monoclinic compound are given (P21/n (No. 11); a=5.3780(1), b=5.4154(1), c=7.6248(2) , b=89.968(2) ). The subsystem CaO-Nb2O5 was re-examined at CaO contents above 70 mol% to clarify inconsistencies in the literature. Two phases were confirmed to form in this region: the polymorphic ordered perovskite Ca4Nb2O9, with solid solution ranging from approximately 17 to 20.5 mol% Nb2O5, and the compound referred to as Ca3Nb2O8, which was shown here to occur as essentially a point compound at the composition 75.25:24.75 CaO:Nb2O5. The perovskite-related structure of the Ca3Nb2O8-type phase was shown to be non-cubic, and further studies are in progress. Capacitance methods at 1 MHz were used to determine the dielectric constants and associated temperature coefficients for eleven compounds in the CaO:Al2O3:Nb2O5 system. Ca2AlNbO6 and Ca3Nb2O8 co-exist in equilibria, and were found to exhibit temperature coefficients of permittivity with opposite signs. Five compositions in the xCa2AlNbO6(1-x)Ca3Nb2O8 system were prepared and their dielectric properties measured by dielectric resonator methods at 5-7 GHZ. The relative permittivities and temperature coefficients of resonant frequency obtained for the end members Ca2AlNbO6 and Ca3Nb2O8 were 30, -88 ppm/ C, and 45, +113 ppm/ C, respectively. Temperature compensation of the resonant frequency was obtained near x=0.67 with a permittivity of 32; no solid solution was detected by X-ray powder diffraction.
Citation: Journal of Solid State Chemistry
Volume: 155 No. 1
Keywords: Ca2AlNbO6,Ca3Nb2O8,calcium niobates,CaO:Al2O3,microwave dielectric properties,Nb2O5,phase diagrams
Research Areas: Materials Science, Ceramics