Publication Citation: Synthesis and properties of turbostratically disordered,ultrathin WSe2 films

NIST Authors in Bold

Author(s): Ngoc Nguyen; Polly Berseth; Qiyin Lin; Catalin Chiritescu; D.G. Cahill; Anastassios Mavrokefalos; Li Shi; Paul Zschack; Michael D. Anderson; Ian M. Anderson; David C. Johnson;
Title: Synthesis and properties of turbostratically disordered,ultrathin WSe2 films
Published: May 11, 2010
Abstract: Turbostratically disordered tungsten diselenide (WSe2) thin films with as few as two c-axis-oriented (basal plane) structural units were synthesized from modulated elemental reactants. By varying the number of elemental W-Se bilayers deposited, the thickness could be controllably varied from two to eighty such structural units. The sample roughness decreases with increasing annealing time and temperature as the crystalline WSe2 basal plane units self assemble from the amorphous precursors. Low angle X-ray diffraction data show that the thickness of the WSe2 films is highly uniform after annealing, with estimated roughness of less than 0.2 nm, and highly oriented, with the c axis of the structural units oriented within 0.1° of the substrate normal as determined from rocking curves of the specular 00l-type diffraction peaks. Pole figures of hk0-type reflections indicate that c-axis-oriented basal plane structural units are randomly oriented within the a-b plane. The widths of diffraction peaks of type hk0, 00l, and hkl (h, k ≠ 0; l ≠ 0) indicate coherence lengths of about (6 to 7) nm in the a-b plane, the full thickness of the film along the c axis, and (1 to 2) nm in mixed-index directions. STEM-HAADF imaging corroborated the X-ray scattering results, providing direct evidence of strong c-axis texture, rotational disorder between adjacent basal plane structural units, and an intraplanar grain size of several nanometers. The combination of intraplanar crystallinity and interplanar rotational disorder explains the significant anisotropy of the thermal conductivity, which is 20 to 30 times higher in the a-b plane than along the c axis. Electrical measurements within the a-b plane indicate that the films exhibit n-type semiconducting behavior.
Citation: Chemistry of Materials
Volume: 22
Issue: 9
Pages: pp. 2750 - 2756
Keywords: chalcogenides, tungsten diselenide, thin film deposition, X-ray diffraction, X-ray reflectivity, STEM Z-contrast imaging, turbostratic disorder, thermal conductivity
Research Areas: Thin-Films, Structures, Materials Science, Chemistry