Transverse Compressive Stress Effect in Y-Ba-Cu-O Coatings on Biaxially Textured Ni and Ni-5at.%W Substrates

Published

June 1, 2003

Author(s)

Najib Cheggour, John (Jack) W. Ekin, Cameron C. Clickner, D. T. Verebelyi, C. L. H. Thieme, Ron Feenstra, P Goyal, D F. Paranthaman

Abstract

Electromechanical properties of yttrium-barium-copper-oxide (YBCO) coatings on both pure Ni and Ni-5at.%W alloy rolling-assisted, biaxially-textured substrates (RABiTS) were investigated. The effect of transverse compressive stress on transport critical-current densities (J_c) was measured on samples at 76 K and self magnetic field. Transverse compressive stress can significantly degrade J_c in YBCO deposited on pure Ni RABiTS unless sufficient frictional support is provided to the sample or the substrate is given a work-hardening treatment. On the other hand, results obtained for YBCO on Ni-5at.%W alloy RABiTS show that the tolerance to transverse stress of these conductors are significantly improved. These electromechanical-property results are interpreted in terms of scanning-electron micrographs of the microstructure of the samples after electromechanical testing, as well as stress-strain characteristics measured on RABiTS substrates at 76 K. The tensile yield strength, Young's modulus, and proportional limit of elasticity of candidate RABiTS substrate materials were tabulated and compared.

Citation

IEEE Transactions on Applied Superconductivity

Volume

13

Issue

2

Pub Type

Journals

Download Paper

Local Download

Keywords

coated conductors, critical current density, mechanical properties, microstructure, RABiTS, strain, stress, YBCO

Citation

Cheggour, N. , Ekin, J. , Clickner, C. , Verebelyi, D. , Thieme, C. , Feenstra, R. , Goyal, P. and Paranthaman, D. (2003), Transverse Compressive Stress Effect in Y-Ba-Cu-O Coatings on Biaxially Textured Ni and Ni-5at.%W Substrates, IEEE Transactions on Applied Superconductivity, [online], https://tsapps.nist.gov/publication/get_pdf.cfm?pub_id=30839 (Accessed April 19, 2024)