Measuring the Structure of Epitaxially Assembled Block Copolymer Domains with Soft X-ray Diffraction

Published

November 30, 2009

Author(s)

Gila Stein, James Alexander Liddle, Andrew Aquila, Eric M. Gullikson

Abstract

The size, shape, and roughness of poly(styrene-b-methyl methacrylate) block copolymer domains assembled on an epitaxial template are characterized with soft x-ray diffraction. The domain size and shape are deformed when the dimensions of the epitaxial template are incommensurate with the equilibrium dimensions of the block copolymer, producing sidewall angles in the range of 1 deg. to 2 deg. (+/-0:2 deg.). The average width of the copolymer interface is (4.9 +/- 0.08) nm. Comparison with mean-field theoretic predictions for the structure of block copolymer interfaces suggests a low-frequency variance in the copolymer interface position of 0.3 nm^2,or a low-frequency line-edge roughness of approximately 1.7 nm. This roughness magnitude is less than predicted by capillary wave models for copolymer interfaces, and may indicate suppression of longer-wavelength fluctuation modes due to substrate pinning or block connectivity.

Citation

Macromolecules

Pub Type

Journals

Download Paper

Local Download

Keywords

line-edge roughness, diblock, self-assembly, directed assembly

Citation

Stein, G. , Liddle, J. , Aquila, A. and Gullikson, E. (2009), Measuring the Structure of Epitaxially Assembled Block Copolymer Domains with Soft X-ray Diffraction, Macromolecules, [online], https://tsapps.nist.gov/publication/get_pdf.cfm?pub_id=903155 (Accessed April 16, 2024)