Experimentally, How Does Cu TSV Diameter Influence its Stress State?

Published

May 27, 2015

Author(s)

Chukwudi A. Okoro, Lyle E. Levine, Yaw S. Obeng, Ruqing Xu

Abstract

In this work, an experimental study of the influence of Cu through-silicon via (TSV) diameter on stress build up was performed using synchrotron-based X-ray microdiffraction technique. Three Cu TSV diameters were studied; 3 µm, 5 µm and 8 µm, all of which were fabricated in a single chip. Prior to the measurements, the die was annealed at 420 °C (30 min), yielding a fully grown and stable microstructure. The measured mean hydrostatic stresses in the Cu TSV were 185±14 MPa (3 µm Cu TSV diameter), 147±10 MPa (5 µm Cu TSV diameter) and 205±15 MPa (8 µm Cu TSV diameter). As such, no conclusive stress dependence on Cu TSV diameter was determined. This is attributed to stress relaxation mechanisms including plastic deformation, grain boundary sliding, dislocation motion and the formation of cracks/ voids which are otherwise neglected in many reported finite element modeling based studies. Additionally, this study underscores that the stress-strain behavior of Cu TSVs are significantly dependent on their thermal history and microstructural characteristics.

Proceedings Title

Proceeding of IEEE Electronic Components and Technology Conference (ECTC)

Conference Dates

May 26-29, 2015

Conference Location

San Diego, CA

Pub Type

Conferences

Citation

Okoro, C. , Levine, L. , Obeng, Y. and Xu, R. (2015), Experimentally, How Does Cu TSV Diameter Influence its Stress State?, Proceeding of IEEE Electronic Components and Technology Conference (ECTC), San Diego, CA (Accessed April 24, 2024)