Publication Citation: Transverse Stress and Fatigue Effects in Y-Ba-Cu-O Coated IBAD Tapes

NIST Authors in Bold

Author(s): John (Jack) W. Ekin; S L. Bray; Najib Cheggour; Cameron C. Clickner; S R. Folytn; P N. Arendt; A A. Polyanskii; David C. Larbalestier; C. N. McCowan;
Title: Transverse Stress and Fatigue Effects in Y-Ba-Cu-O Coated IBAD Tapes
Published: January 08, 2001
Abstract: Measurements of the effects of static and cyclic (fatigue) transverse stress on the critical current of Ya-Ba-Cu-O-coated tapes made by ion-beam-assisted deposition (IBAD) are reported at 76 K in self magnetic field. Ya-Ba-Cu-O films (~15m thick) on Inconel substrates (100 5m thick) with IBAD buffer layers had critical-current densities (Jc) exceeding 1 MA/cm2 and n values of about 50 (where n is an index of the sharpness of the superconductor-to-normal transition). Under static loads of 100 Mpa, the degradation in Jc was less than 5% (7% at 120 Mpa). When subjected to cyclic loading, there was less than 2% additional Jc degradation after 2000 fatigue cycles. Microscopic examination of the samples indicates that this limited Jc degradation may have arisen from longitudinal cracks forming near the edges of the sample after being subjected to these high transverse pressures. This fracture mode would indicate that longitudinal side support from high-yield substrates or epoxy impregnation of magnet structures may provide additional tolerance against Jc degradation from transverse stress.
Citation: IEEE Transactions on Applied Superconductivity
Volume: 11
Issue: 1
Pages: pp. 3389 - 3392
Keywords: coated conductors,critical current,electromechanical,IBAD,mechanical,stress,transverse stress